40Cr_牌號

　　40CR材料

　　40CR鋼屬于中等碳調節的鋼。鋼價中等且易于加工。經過適當的熱處理后，可以獲得韌性，塑料和磨損的耐藥性。陽性火可以促進組織ballization并提高粗糙的加工性（硬度 <160HBW).The ignition of 550-570 ° C has the best comprehensive mechanical performance.The hardening of the steel is higher than 45 steel, which is suitable for high -frequency quenching, flame quenching and other surfaces and hardening treatment.

　　After the quality adjustment, it has good comprehensive force and incompleteness, good low temperature impact toughness and low gap sensitivity.The hard quenchtability of the steel is good, and it can be quenched to φ28 ~ φ60mm during water quenching, and it can be quenched to φ15 ~ φ40mm during oil quenching.In addition to the quality adjustment, the steel is also suitable for carbon nitrogen penetration and high -frequency induction quenching treatment.The processability is better. When the hardness is 174 to 229HBW, the relative processability is 60%.

　　40CR supply status

　　Antuction, hardness ≤207hbw.

　　40CR chemical composition

　　According to the standard GB/T3077-1999, the chemical composition of the steel (physical score): C0.37%～ 0.44%, Si0.17%～ 0.37%牌號, MN0.50%～ 0.80%, CR0.80%～ 1.10%, Ni ≤ 0.30%.

　　40CR corresponding material

　　China GB standard number 40CR, German DIN standard material number 1.7035/1.7045, German DIN standard brand 41CR4/42CR4, British EN standard brand 18, British BS standard number 41CR4, French AFNOR standard brand 42C4, French NF standard number 38CR4/41CR4, Italy UNI Standard Dame Number 41CR4, Belgian NBN Standard Brand 42CR4, Swedish SS Standard Brand 2245, Spanish UNE Standard Brand 42CR4, Japan JIS Standard Script SCR440 (H)/SCR440, American ASIS/SAE/ASTM standard number 5140, ISO standard brand number 41CR4.

　　40CR physical performance

　　Critical point temperature (approximate value): ACCM = 780 ° C, AC1 = 780 ~ 770 ° C, AC3 = 840 ~ 805 ° C, ms = 335-328 ° C.

　　Wiring expansion coefficient: temperature 20 ~ 200 ℃/20 ～ 300 ℃/20 ~ 400 ℃/20-500 ℃/20-600 ℃

　　/20 ～ 700 ℃, line expansion coefficient (11.9 ~ 12.0) × 10-6k-1/(13.3 ~ 13.4) × 10-6k-1/(14.3 ~ 14.4) × 10-6k-1/(15.0 ～ 15.1) × 10-6k-1/(15.3 ～ 15.4) × 10-6k-1/(15.4 ~ 15.5) × 10-6k-1.

　　Thermal guidance rate: temperature 100 ℃/200 ℃/300 ℃/400 ℃/500 ℃/600 ℃, thermal conductivity 32.6 [w/(m · k)]/25.5 [w/m · k)].

　　40CR thermal processing specification

　　The heating temperature is 1150 ~ 1200 ° C, the start temperature starts at 1100 ~ 1150 ° C, the termination temperature is> 800°C和冷卻方法：直徑大于60mm時，緩慢冷。

　　40CR正常退火規格

　　退火溫度為825?845°C，保存時間，爐子冷，硬度≤207hbw。

　　40CR完全退火規格

　　退火溫度為860?890°C，保存為2至3H，爐子冷后冷至500°C。

　　40CR陽性規格

　　正火的溫度為850?870°C，熱量是同一時間，空氣冷，硬度≤250hbw。

　　40CR冷壓粗糙軟化處理規范

　　柔軟度溫度為740?760°C，保留熱量為4至6H，然后以5-10°C/h至≤600°C的冷速度冷卻。

　　治療前的硬度≤217HBW，治療后硬度≤163HBW。

　　40CR高溫回收規范

　　恢復溫度為680?700°C，冷卻至≤600℃，空氣冷卻，硬度≤207hbw。治療前的硬度≤217HBW，治療后硬度≤163HBW。

　　40CR出生鐵面粉保護規范規范

　　（670±10）℃×2H，用爐子加熱，（710±10）°C×2H，用爐子冷卻，（670±10）℃×2H，增加爐子的加熱，（710±10 ）°C×2H，然后跟隨關注者，跟隨跟隨者冷卻爐子（670±10）°C×2H，用爐子加熱，（710±10）°C×2H，總共三個循環，然后冷卻至550°C，空氣冷卻，在處理后，硬度為153HBW。

　　40CR質量調整規范

　　淬火溫度（850±10）°C，油冷卻，點火溫度（520±10）°C，水或油冷卻。硬度≤250hbw。

　　40CR普通淬火和恢復規格

　　淬火溫度為830?860°C，油冷，火為400?600°C，水或油在冷卻。

　　40cr淬火+恢復+硼滲流過程

　　850°C淬火，在400°C下捕獲，硬度40?45hrc; Boono鹽浴配方（質量評分）：NACL15％+NA2B4O771％+SIC11％（SIC為140個網格粉末）；到850°C，恢復了400°C×40分鐘，峰值的深度為0.06至0.08min，硬度為1200hv0.1。

　　40CR樁焊接維修過程

　　清潔污垢，保護二氧化碳氣體的焊接，焊接線號H08MN2SIA，直徑0.8mm，焊接電流100a的焊接電流，18-21V的電弧電壓，使用短電路過渡，首先將零件均勻旋轉至點燃電弧焊接，以便可以使用焊接道來制作焊接徑。當通過螺旋向前推動時，焊接軌道均勻加熱以防止軸變形。

　　控制零件在200°C下的表面溫度，焊接后加熱，并冷卻。

　　40CR使用

　　可用于拉動霉菌和整形手術。

　　它可用于冷擠壓打孔，重載的冷頭，小打孔頭和直徑 <5-6mm in a thick steel plate in 10 to 25mm.

　　它可用于中型和小沖洗，小型服務壽命冷泵工具。

　　原鐵碎屑的恢復規格可用于冷壓形成模具。

　　粉末冶金壓力。

　　在深層拳頭Quench+恢復+硼滲漏處理后，平均使用壽命為10500，這增加了W18CR4V鋼打孔的使用壽命的2至3倍。

　　使用40CR鋼柱插頭進行淬火+恢復+硼滲漏，而不是CR12MOV鋼淬滅+恢復，使用壽命已從37,000增加到42,000件增加到44牌號,000件。

　　40CR鋼硼傾倒頭代替W18CR4V高速鋼服務壽命已從1,000件增加到2500件。

　　40CR鋼鍛造熱淬火+實心硼稀土滲漏+淬火+低溫恢復過程而不是5Crmnmo鋼訂單

　　活塞熱鍛造體支柱上的模具已從1500增加到2,000。

　　可用于預測桿。

　　它可用于制造具有較大尺寸，復雜形狀和高精度的塑料模具。

　　可用于中型塑料模具。